Direct quantification of mechanical responses of TiSiN/Ag multilayer coatings through uniaxial compression of micropillars

Keyphrases

• Direct Quantification 100%
• Uniaxial Compression 100%
• Mechanical Response 100%
• Micropillar 100%
• TiSiN(Ag) 100%
• Multilayer Coatings 100%
• Layer Thickness 40%
• Fracture Strength 40%
• Elastic Response 40%
• Elastic Modulus 20%
• Deformation Behavior 20%
• Uniaxial 20%
• Scanning Electron Microscopy 20%
• Plastic Deformation 20%
• Deformation Mechanism 20%
• Failure Mechanism 20%
• Size Effect 20%
• Stress-strain Curve 20%
• Linear Elastic 20%
• Yield Point 20%
• Strength Failure 20%
• Failure Behavior 20%
• Brittle Failure 20%
• Electron Microscopy Observations 20%
• Fracture Failure 20%
• Fracture Point 20%
• Arc Ion Plating 20%
• Strength Mechanism 20%
• Uniaxial Compression Test 20%
• In-situ Microcompression 20%
• TiSiN 20%
• Fracture Deformation 20%
• Ag Layer 20%
• Total Strain 20%
• Micropillar Compression Test 20%
• Micropillar Compression 20%

Engineering

• Mechanical Response 100%
• Multilayer Coating 100%
• Layer Thickness 66%
• Compression Test 66%
• Fracture Strength 66%
• Elastic Response 66%
• Micropillar Compression 66%
• Deformation Behavior 33%
• Young's Modulus 33%
• Plastic Deformation 33%
• Failure Mechanism 33%
• Size Effect 33%
• Yield Point 33%
• Stress-Strain Curve 33%
• Failure Behavior 33%
• Brittle Failure 33%
• Fracture Failure 33%
• Fracture Deformation 33%

Material Science

• Fracture Toughness 100%
• Elastic Moduli 50%
• Scanning Electron Microscopy 50%
• Plastic Deformation 50%
• Arc Ion Plating 50%