Improved efficiency of dye-sensitized solar cells by design of a proper double layer photoanode electrodes composed of Cr-doped TiO2 transparent and light scattering layers

M. R. Mohammadi (Lead / Corresponding author), A. M. Bakhshayesh, F. Sadri, M. Masroor

    Research output: Contribution to journalArticlepeer-review

    20 Citations (Scopus)

    Abstract

    A new strategy for enhancing the efficiency of TiO2 dye-sensitized solar cells (DSSCs) by design of a new double layer film doped with Cr ions, with various morphologies, is reported. X-ray diffraction and field emission scanning electron microscope (FE-SEM) analyses revealed that the synthesized nanoparticles had uniform and nanometer grains with different phase compositions and average crystallite size in the range of 10-12 nm depending upon Cr atomic percentage. UV-vis absorption showed that Cr introduction enhanced the visible light absorption of TiO2 nanoparticles by shifting the absorption onset to visible light region. Furthermore, the band gap energy of nanoparticles decreased with an increase in dopant concentration due to reduction of particle size. It was found that, 3 at.% Cr-doped TiO 2 DSSC in the form of a double-layer film composed of TiO2 nanoparticles, as the under-layer, and mixtures of nano- and micro-particles with weight ratio of 80:20, as the over-layer, (i.e., CT3/NM3 solar cell) had the highest power conversion efficiency of 7.02 %, short current density of 17.32 mA/cm2 and open circuit voltage of 674 mV. This can be related to achievement of a balance among the electron injection, light scattering effect and dye sensitization parameters. Optimization of light scattering effect of photoanode electrode led to improve the photovoltaic performance of CT3/NM3 double-layer solar cell and was demonstrated by diffuse reflectance spectroscopy. The presented strategy would open up new insight into fabrication of low-cost TiO2 DSSCs with high power conversion efficiency.

    Original languageEnglish
    Pages (from-to)77-87
    Number of pages11
    JournalJournal of Sol-Gel Science and Technology
    Volume67
    Issue number1
    DOIs
    Publication statusPublished - 30 Apr 2013

    Keywords

    • Cr-doped TiO
    • Double layer film
    • Dye-sensitized solar cell
    • Light scattering effect

    Fingerprint

    Dive into the research topics of 'Improved efficiency of dye-sensitized solar cells by design of a proper double layer photoanode electrodes composed of Cr-doped TiO<sub>2</sub> transparent and light scattering layers'. Together they form a unique fingerprint.

    Cite this